Standard: ASTM A335
grade:P1, P2,P5,P9,P11,P91,P92
OD:10.3-660mm
WT:1.6-60mm
Length:5.8m-12m or random legth
Technical: Quenching & Tempering
Application: Gas fire power plant, coal fire power plant, headers and steam lines, Feedwater pipes, superheaters, and reheaters.
ASTM A335 Pipe (ASME S/A335, Chorme-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Sometimes referred to as “P Grade”, chome moly pipe is popular in P-Grades P5, P9, P11, P22, and P91. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries.
A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (Mo) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability.
ASTM A335 alloy steel pipes fit ASTM A234 WPx series buttweld fittings (WP5, WP9, WP91) and A182 Fx forged fittings and flanges (A182 F5, F9, F11, F22, F91). All these materials have similar chemical and mechanical properties and can be joined or welded.
CHEMICAL COMPOSITION
The types of alloy steel covered by the ASTM A335 – ASME SA335 specification are designed with a “P” prefix, from P5 to P92. Grades P11/P22 and P91/92 are typically found in power stations, whereas grade P5 and P9 are more common for application in the petrochemical industry. Grades P9 and P91 are in the list, the more expensive (a P91 seamless pipe may cost approx 5€ per kg.).
ASTM A335 Low-Alloy Steel (Grades) |
UNS equivalent |
C≤ | Mn | P≤ | S≤ | Si≤ | Cr | Mo |
P1 | K11522 | 0.10~0.20 | 0.30~0.80 | 0.025 | 0.025 | 0.10~0.50 | – | 0.44~0.65 |
P2 | K11547 | 0.10~0.20 | 0.30~0.61 | 0.025 | 0.025 | 0.10~0.30 | 0.50~0.81 | 0.44~0.65 |
P5 | K41545 | 0.15 | 0.30~0.60 | 0.025 | 0.025 | 0.5 | 4.00~6.00 | 0.44~0.65 |
P5b | K51545 | 0.15 | 0.30~0.60 | 0.025 | 0.025 | 1.00~2.00 | 4.00~6.00 | 0.44~0.65 |
P5c | K41245 | 0.12 | 0.30~0.60 | 0.025 | 0.025 | 0.5 | 4.00~6.00 | 0.44~0.65 |
P9 | S50400 | 0.15 | 0.30~0.60 | 0.025 | 0.025 | 0.50~1.00 | 8.00~10.00 | 0.44~0.65 |
P11 | K11597 | 0.05~0.15 | 0.30~0.61 | 0.025 | 0.025 | 0.50~1.00 | 1.00~1.50 | 0.44~0.65 |
P12 | K11562 | 0.05~0.15 | 0.30~0.60 | 0.025 | 0.025 | 0.5 | 0.80~1.25 | 0.44~0.65 |
P15 | K11578 | 0.05~0.15 | 0.30~0.60 | 0.025 | 0.025 | 1.15~1.65 | – | 0.44~0.65 |
P21 | K31545 | 0.05~0.15 | 0.30~0.60 | 0.025 | 0.025 | 0.5 | 2.65~3.35 | 0.80~1.60 |
P22 | K21590 | 0.05~0.15 | 0.30~0.60 | 0.025 | 0.025 | 0.5 | 1.90~2.60 | 0.87~1.13 |
P91 | K91560 | 0.08~0.12 | 0.30~0.60 | 0.02 | 0.01 | 0.20~0.50 | 8.00~9.50 | 0.85~1.05 |
P92 | K92460 | 0.07~0.13 | 0.30~0.60 | 0.02 | 0.01 | 0.5 | 8.50~9.50 | 0.30~0.60 |
MECHANICAL PROPERTIES
A335 Low-Alloy Pipe | UNS Number | Yield Strength ksi | Tensile Strength ksi | Elongation % | Rockwell | Brinell |
P1 | K11522 | 30 | 55 | 30 | – | – |
P2 | K11547 | 30 | 55 | 30 | – | – |
P5 | K41545 | 40 | 70 | 30 | – | 207 max |
P9 | S50400 | 30 | 60 | 30 | – | – |
P11 | K11597 | 30 | 60 | 20 | – | – |
P12 | K11562 | 32 | 60 | 30 | – | 174 max |
P22 | K21590 | 30 | 60 | 30 | – | – |
P91 | K91560 | 60 | 85 | 20 | – | – |
TESTING REQUIREMENTS
- Transverse/longitudinal: tension and flattening, hardness, bend tests- for material that has been heat-treated in batch furnaces, these tests shall be made on the 5% of the pipes from each heat lot number. For smaller lots, one pipe at a minimum has to be tested
- ASTM A335 Gr. P91 shall have a hardness of 250 HB / 265 HV (25 HRC)
- Hydro testing: shall be applied to every length of pipe
- The non-destructive electric test is optional
TOLERANCES
DIAMETER
A335 Pipe | Over | Under | ||
NPS [DN] | in. | mm | in. | mm |
1/8 to 1 1/2 / DN 6 to 40 | 1/64 (0.015) | 0.4 | 1/64 (0.015) | 0.4 |
Over 1 1/2 to 4 / DN 40 to 100 | 1/32 (0.031) | 0.79 | 1/32 (0.031) | 0.79 |
Over 4 to 8 / DN 100 to 200 | 1/16 (0.062) | 1.59 | 1/32 (0.031) | 0.79 |
Over 8 to 12 / DN 200 to 300 | 3/32 (0.093) | 2.38 | 1/32 (0.031) | 0.79 |
Over 12 / > DN 300 | +/- 1% of the specified outside diameter |
WALL THICKNESS
The tolerances in WT, in %, from specified are:
- 1/8 to 2 1/2 [6 to 65] incl., all t/D ratios: over 20%, under 12.5%
- Above 2 1/2 [65], t/D < or = 5%: over 22.5%, under 12.5%
- Above 2 1/2 [65], t/D > 5%: over 15%, under 12.5%
t = Specified Wall Thickness; D = Specified Outside Diameter)
ALLOY PIPE CROSS REFERENCE TABLE ASTM vs. EN GRADES
Chrome Moly Pipes: Werkstoff vs EN vs ASTM | ||
---|---|---|
Werkstoff /DIN | EN | ASTM |
1.5415 | 16Mo3 | A335 Grade P1 |
1.7335 | 13CrMo4-5 | A335 Grade P11, P12 |
1.7380 | 10CrMo9-10 | A335 Grade P22 |
1.7362 | X11CrMo5 | A335 Grade P5 |
A335 Grade P9 | ||
1.4903 | X10CrMoVNb9-1 | A335 Grade P91 |